Purpose: The purpose of this study was to investigate the diametral tensile strength of polymer-based temporary crown and fixed partial denture (FPD) materials, and the change of the diametral tensile strength with time.
Material and Methods: One monomethacrylate-based temporary crown and FPD material (Trim) and three dimethacrylate-based ones (Protemp 3 Garant, Temphase, Luxtemp) were investigated. 20 specimens (?. 4 mm × 6 mm) were fabricated and randomly divided into two groups (Group I: Immediately, Group II: 1 hour) according to the measurement time after completion of mixing. Universal Testing Machine was used to load the specimens at a cross-head speed of 0.5 mm/min. The data were analyzed using one-way ANOVA, the multiple comparison Scheffe test and independent sample t test (α= 0.05).
Results: Trim showed severe permanent deformation without an obvious fracture during loading at both times. There were statistically significant differences among the dimethacrylate-based materials. The dimethacrylate-based materials presented an increase in strength from 5 minutes to 1 hour and were as follows: Protemp 3 Garant (23.16 - 37.6 MPa), Temphase (22.27 - 28.08 MPa), Luxatemp (14.46 - 20.59 MPa). Protemp 3 Garant showed the highest value.
Conslusion: The dimethacrylate-based temporary materials tested were stronger in diametral tensile strength than the monomethacrylate-based one. The diametral tensile strength of the materials investigated increased with time.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.
Total Visit :10,451,932
Total Download :4,406,636
Today View :804
Ajou University Medical Information & Media Center 164 Worldcup-ro Yeongtong-gu Suwon 16499 Korea / TEL : 031-219-5312 Copyright (c) Ajou University Medical Information & Media Center All Rights Reserved. AJOU Open Repository는 국립중앙도서관 OAK 보급사업으로 구축되었습니다.